Platin Elektrolyt 6 G./Liter

Platinum Electrolyte - Platinum Bath - Platinizing with Betzmann Electroplating 

Platinum is characterized by high abrasion resistance and gives a noble gray surface.

Alternative: White palladium

The platinum bath from Betzmann Galvanik deposits corrosion-resistant, very bright and shiny platinum layers up to a thickness of 0.5 - 1.0 µm.

It is suitable for both decorative and technical applications and is very well suited for pin, bath and pad electroplating!..

Operating data:

Platinum content: 6.0 g/L

pH-value: <1

Density: 1.08 g/ml, increasing

Working conditions:

Voltage: from 3 volts

Bath temperature: 30 - 40 °C

Exposure time: 2 - 4 min.

Anode material: platinized titanium

Anode/cathode surface: 1 : 1

Fabric movement: required

Recommended speed: 2 - 8 cm/sec.

Deposition rate: approx. 11 mg/Amin; approx. 0.5-1.5 A/dm2

Bath movement: recommended

Precipitation data:

Hardness: 500 HV

Layer thickness: max. 1.0 µm

Fineness: 99,9%

Delivery form: 

Ready to use 6 g/L Pt

Operating Conditions and Deposit Data

Notes:

• We strongly advise against the use of stainless steel anodes for most of our plating processes.
• Higer voltages give greater plating rates, however more gas is liberated and a mist mask is recommended.
• Plating rates are calculated over a sample area which is permanently covered by swab.
• Will plate directly onto freshly prepared nickel or stainless steel.