MetaSeal - Metal Care

Gold Electrolyte – 2 g/L Gold Plating Solution (BMG-077-TG-2GM)Brilliant, Durable Gold CoatingsOur high-quality Gold Electrolyte (2 g/L) allows uniform, brilliant, and long-lasting gold plating. Perfect for jewelry, technical parts, and professional applications requiring high corrosion resistance, conductivity, and optical perfection.Suitable for bath plating, brush plating, and pad plating.💡 Note: Always ensure proper cleaning and surface preparation for best results.Key Benefits✔ Bright, mirror-like gold finish✔ Excellent wear and abrasion resistance✔ High corrosion and tarnish protection✔ Uniform, adhesive coatings✔ Suitable for bath, brush, and pad plating✔ Ideal for jewelry, watches, and technical components✔ Can be combined with palladium or rhodium pre- and post-coatingsTechnical SpecificationsParameterValue / RecommendationGold Content2 g/LVoltage (Bath)2.0 – 4.0 VVoltage (Brush/Pad)3.0 – 6.0 VTemperature20 – 40 °CpH Valuestrongly acidicElectrodesPlatinum or titaniumCoating Colorbright yellow goldLayer Thickness0.1 – 2 µm (adjustable)Depositionuniform & controllable💡 Pro Tip: A pre-layer of palladium improves adhesion and reduces surface imperfections.ApplicationsJewelry (rings, chains, gold alloys)Watches and luxury itemsElectrical contacts and connectorsPrecision technical componentsDecorative and protective coatingsApplication – Step by StepClean & degreaseActivate surfacePre-plating (optional but recommended) – palladium or nickelGold plating – bath, brush, or padPost-treatment – rinse, dry, optional protective layer💡 Pro Tip: Use a clean platinum electrode and proper current density to achieve the most uniform, high-brightness finish.CompatibilityElectroplating bathsBrush plating devicesPad plating systems👉 Can be combined with:Palladium or rhodium pre-coatingCorrect electrodes and fabric padsPractical ExamplesGold-plated rings and chains with high brillianceTechnical contacts with wear-resistant gold finishDecorative items with precise, even gold layersFAQWhy use gold electrolyte?For a brilliant, conductive, and corrosion-resistant gold layer.How thick should the gold layer be?Depends on application: decorative 0.1–0.5 µm, technical 1–2 µm.Is it suitable for beginners?Yes, with proper cleaning, activation, and controlled current.Which electrode works best?Platinum electrodes produce the most stable, uniform results.Recommended AccessoriesPower supply / rectifiersElectrodes (Platinum / Titanium)Cleaners & activatorsGalvanic plating systemsOrder Gold Electrolyte 2 g/L NowAchieve high-brightness, durable, professional gold coatings for jewelry, electronics, and technical applications.👉 Order now and create perfect surfaces.

Metal Polish Ultra – The Perfect Pre-Treatment for Premium Plating Quality For electroplating professionals and anyone who demands the highest surface quality: Metal Polish Ultra delivers industry-leading cleaning power and surface preparation for the best plating results. Ultimate Cleaning Power – Ideal Adhesion and Surface Prep This advanced formulation reliably removes: even very stubborn silicone and release agent residues embedded wax and polishing compounds fine contaminants and particulates unwanted metal films and oxidation products The built-in cleaner ensures deep-cleaned surfaces that form the ideal base for uniform, high-adhesion plating layers. Restore and Enhance Surface Brilliance Whether for restoration, repair, or high-end surface finishing, this premium polish combined with a fine microfiber cloth delivers: brilliant shine on chrome surfaces smooth, reflective results on conductive plastics effective removal of accidental coatings (e.g., gold) Challenging substrates are treated gently while still achieving a radiant finish. Key Benefits at a Glance Perfect pre-treatment for bath, brush, and swab plating Removes stubborn residues and embedded soils Improves adhesion and coating quality Suitable for metals, chrome, and conductive plastics Easy and controlled application Designed for workshop, professional labs, and industrial use Result: Technically pristine surfaces, enhanced coating performance, and an exceptional finish every time.

Rust Remover from Betzmann Galvanik! Rust remover - Rust Ex from Betzmann GalvanikThe combination of effective chemicals and selected polishing agents results in a unique formula for reviving heavily corroded metal objects. Corrosion inhibitors prevent attack on non-corroded parts. Economical and easy to use. Ideal for treating large areas of iron, bronze, copper, steel, etc. Ingredients: AQUA, ALUMINA, HYDROCHLORIC ACID, fatty alcohol polyglycol ether, fatty acids, 2-propyn-1-ol, compound with methyloxirane, XANTHAN GUM, COCAMIDOPROPYL BETAINE , prop-2-in-1-ol. Information on ingredients according to the Detergents Directive - Annex VII D, EC -648/2004 is available on the EU portal "European List of Cosmetic Ingredients".        GHS05 GHS07  Danger. Causes severe skin burns and eye damage. May cause respiratory irritation. If medical advice is needed, have packaging or label at hand. Keep out of the reach of children. Wear protective gloves / protective clothing / eye protection / face protection. Do not breathe vapor. IF ON SKIN (or hair): Remove all contaminated, soaked clothing immediately. Wash skin with water/shower. IF IN EYES: Rinse cautiously with water for several minutes. Remove existing contact lenses if possible. Continue to rinse. Contains: Fatty alcohol polyglycol ether, hydrochloric acid.  

Gold Electrolyte BMG‑072 – High Speed Gold High-Quality High-Speed Gold Plating Electrolyte – 12 g Gold per Liter Short Description The Gold Electrolyte BMG‑072 (High Speed Gold) is a ready-to-use plating solution for fast and high-quality gold deposition on metal surfaces. With 12 grams of gold per liter, this electrolyte allows faster deposition, thicker layers in less time, and coverage of larger areas compared to lower-concentration gold baths. Its hard, uniform, and well-adhering gold layers make it suitable for hobbyists, workshops, labs, and professional industrial applications. Applications High Speed Gold Electrolyte is ideal for: Decorative gold plating (jewelry, pendants, trims) Technical gold plating (contact surfaces, circuit boards, measuring devices) Corrosion protection and durable surface finishing Multi-layer systems, e.g., Copper → Nickel → Gold Partial or full coverage of complex components The higher gold content allows faster results and higher deposition rates than standard gold baths. How it Works (Simple Explanation) Gold is deposited onto metal surfaces through direct current: Polish: Prepare a smooth, high-gloss surface. Clean: Thoroughly degrease (e.g., with an electrocleaner). Activate: Chemically activate the surface (e.g., with an activator). Gold Plating: Apply DC (approx. 4 V) with a platinum or graphite anode to deposit gold. Result: a hard, uniform gold layer with excellent gloss and high durability. Advantages High gold content (12 g/L) for faster deposition and thicker layers Very hard and uniform layers, even for prolonged plating Excellent coverage and adhesion on metals like stainless steel, copper, silver, brass, nickel, iron, and steel Suitable for tank, brush, and tampon plating Versatile for decorative and technical plating in hobby, industrial, or research applications Economical for larger surfaces or frequent use Technical Parameters PropertyValue / RangeElectrolyte typeGold plating solution (High Speed Gold)Gold contentapprox. 12 g/LOperating temperature14–25 °CVoltage range3.0–8.0 V (starting at ~4 V)Recommended anodePlatinum or graphiteGold content in depositapprox. 99.9 % (rest carbon)Deposition rateapprox. 0.7 µm/min at 3.5 V (Platinum anode)Layer hardnessapprox. 220–230 HVDeposit densityapprox. 19.0 g/cm³Voltage stressmediumStorageprotect from direct sunlightShelf life1–2 yearsHazard classHarmful / Irritant Note: Values are typical operational data; slight variations may occur depending on application. Application Instructions Surface preparation: Polish → Degrease → Activate Gold plating: Operate the electrolyte at ~4 V with a platinum or graphite anode Partial plating: Mask areas as needed (e.g., tape, nail polish) Sloped surfaces: Use a leveling agent or thickener to reduce material loss Safety Instructions Gold electrolytes contain chemicals and must be handled safely: Wear chemical-resistant gloves, safety glasses, and protective clothing Avoid contact with skin and eyes Rinse immediately with water if contact occurs Use only in well-ventilated areas Do not inhale vapors or aerosols Contains small amounts of potassium cyanide (~0.3%) – handle with care Do not ingest; keep out of reach of children Scope of Delivery Gold Electrolyte BMG‑072 – High Speed Gold Quantity according to selection Conclusion The Gold Electrolyte BMG‑072 (High Speed Gold) is a powerful, professional gold plating solution offering faster deposition rates and thicker layers than standard gold baths. It is ideal for decorative, technical, and industrial applications and adheres well to a broad range of metals, including stainless steel, brass, nickel, and steel. Its combination of high gold content, rapid deposition, and ease of use makes it perfect for hobbyists, workshops, and professionals seeking high-quality, durable, and shiny gold surfaces.